Silicone-acrylate copolymer latex was prepared through three different polymerization processes, i.e., the batch process, preemulsified monomer addition and the monomer addition process. The results revealed that the monomer addition process is a desirable approach to produce narrow particle size distribution latex with higher polymerization conversion and less amount of coagulum. The effect of silicone content on the glossiness and water absorption of latex film was investigated and the results showed that the glossiness of latex film is improved up to a silicone content of 10% of total monomers, but becomes impaired thereafter, whereas water absorption is reduced accordingly.

[1] Kozakiewicz J;Rosciszewski P;Rokicki G;Koldonski G Skarzynski J and Koncka-Foland A .[J].Surface Coatings International Part B:Coatings Transactions,2001,84:243.

[2] Park H S;Yang I M;Wu. J.P;Kim MS Hahm HS Kim SK and Rhee HW .[J].Journal of Applied Polymer Science,2001,81:1614.

[3] Harui N;Agawa T .[J].Coatings Technology,1998,70(880):73.

[4] Mazurek M;Kinning D J;Kinoshita T .[J].Journal of Applied Polymer Science,2001,80:159.

[5] Li.S.Q;Xia. Y.Z;Shi. S.X. a .[J].Beiing Univ Chem Technol in Chinese),2002,29(03):32.

[6] Kokko J .[J].Journal of Applied Polymer Science,1993,47:1309.

[7] Kong X Z;Kan C Y;Luo D;Yuan Q .[J].Chemical Journal of Chinese Universities,1995,16:1810.

[8] Wu Y;Duan H D;Yu Y Q;Zhang CG .[J].Journal of Applied Polymer Science,2001,79:333.

[9] Kan C Y;Liu D S;Kong X Z;Zhu XL .[J].Journal of Applied Polymer Science,2001,82:3194.